1/16" 202XL ULTIMATE HIGH STRENGTH BRAZING ALLOY

  • ITEM#: EG20270000
  • STANDARD PACK: 5 LB
  • SHIPPING:
  • RESTRICTIONS: none

Price available after Registration or Login

Quantity

Product Description

The Elite™ 
Combination Brazing and Buildup Alloy 

The Elite is a flux-coated brazing alloy with high tensile strength and exceptional ductility for joining all types of metals. 
  • High-strength joints — for dependable repairs 
  • High capillarity — thin flowing action allows complete joint fills 
  • Low temperature — easy to use for most maintenance applications 
  • Narrow plastic range — allows control of the heat input to build up, shape or flow into joints 
  • Versatile — joins steel, copper, brass, bronzes, cast iron, tungsten carbide, refractory metals and nickel alloys
  • Cadmium free and low fume coating
SPECIFICATIONS
  • Joint strength: up to 100,000 psi/689 MPa
  • Hardness: 120 BHN
  • Plastic range: approximately 30°F/17°C
  • Working temp: approximately 1686°F/918°C
  • Electrical conductivity: 8% IACS
  • Flux Coating Color: Red
  • Machinability: .. Excellent

PROCEDURES
For Brazing:
Even though 202 XL bonds well through rust, oil, dirt, etc., best results will be obtained by cleaning the weld area. Parts to be joined should have a joint clearance of 0.003 inch. Using a neutral flame, heat the base metal to a dull red. Melt off a small amount of rod and flux, allowing thin deposits to flow through the joint. Add additional filler metal as needed. Allow the completed joint to cool at room temperature.

For Buildup and Overlaying:
202 XL can be applied on any moderately clean surface. Whenever possible, clean the weld area by removing surface dirt and fatigued metal. Preheat only the starting weld area to a dull red. Apply filler metal by placing the tip of the rod and the tip of the flame cone (neutral flame) in contact with the base metal. Melt the metal in tinning fashion. Keep the torch angle at 70° to the base metal. To apply a pass-on-pass buildup, return to the start of the first bead. With the torch angle lowered to 20°, apply successive layers of filler metal until the desired height is obtained.

1/16" 202XL ULTIMATE HIGH STRENGTH BRAZING ALLOY

202 Xl
Brazing
All Metals Except White Metals
Joining° Build-Up° Overlay
1/16" x 18"
Flux-Coated Brazing Rod
X-Ergon

1/16" 202XL ULTIMATE HIGH STRENGTH BRAZING ALLOY

202 Xl
Brazing
All Metals Except White Metals
Joining° Build-Up° Overlay