Hi-Braze™
General-Purpose Silver Brazing Alloy
Hi-Braze is a low working temperature silver brazing alloy with superb wetting
action on difficult-to-join metals such as tool steels, stainless steel, beryllium
copper and nickel alloys.

• Fast flowing — works well on tight joints
• High silver content — lower melting point and reduces need for high heat for joining
• High-detergent flux — cleans metal for strong joints
• High electrical conductivity
• High strength
• Corrosion resistant
• Cadmium free

SPECIFICATIONS

• Joint strength: up to 60,000 psi/414 MPa
• Elongation: 32%
• Working temperature: 1370°F/743°C
• Electrical conductivity: 19% IACS
• Corrosion resistance: Good
• Coating: Blue

PROCEDURES
Clean the weld area. Remove all rust, paint, grease, oil and other foreign matter. Maintain joint clearance of 0.003” to 0.005”. Prefluxing is not required; however, additional flux will help in tight joints and may be needed. Heat the weld area to a dull red color using a slightly carburizing flame. Melt off a small amount of alloy and flux. Keep the torch in motion and flow the deposit through the joint. Allow to cool slowly. Remove flux residue with warm water.